Factory Price Waterproof Transparent Electronic Potting Compound Silicone Rubber for LED Screen
Description
Electronic potting compound silicone rubber is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time.
Application
Electronic potting compound silicone rubber is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB, substrate, etc.
Data Sheets of Electronic potting Compound Silicone Rubber:
TECHNICAL GUIDELINES
1, Typical Application
It could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
- It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Mixing Ratio: part A: part B = 1:1
3, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
4, Pls note that the thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100ºC, the silicone will cure in 15 minutes; while in 25ºC room temperature, the silicone will cure around 8 hours.
PACKAGE:
20Kg/pail as a set (Part A 10Kg + Part B 10Kg)
Advantages of Hong Ye Silicone
Any questions about silicone rubber pls fell free to contact Jelly~
whatsup: 00 86 18938867561
Electronic potting compound silicone rubber is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time.
Application
Electronic potting compound silicone rubber is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB, substrate, etc.
Data Sheets of Electronic potting Compound Silicone Rubber:
| Model | Color | Viscosity (cps) | Hardness (A°) | Mixing ratio | Operating Time(min) | Curing Time(hr, 25ºC) | Thermal conductivity{w(m.k)} | dielectric strength(kV/mm) | dielectric constant(1.2MHz) | Volume resistivity(Ω.cm) | coefficient of linear expansion{m/(m.k)} | flame retardation |
| HY-9025 | Grag | 500±500 | 25±5 | 1:1 | 30~60 | 4~5 | ≥0.2 | ≥25 | 3.0-3.3 | ≥1.0x10*16 | ≤2.2x10*-4 | 94-V0 |
| HY-9045 | Grag | 2500±500 | 45±5 | 1:1 | 30~60 | 4~5 | ≥0.2 | ≥25 | 3.0-3.3 | ≥1.0x10*16 | ≤2.2x10*-4 | 94-V0 |
| HY-9055 | Grag | 3000±500 | 55±5 | 1:1 | 30~60 | 4~5 | ≥0.2 | ≥25 | 3.0-3.3 | ≥1.0x10*16 | ≤2.2x10*-4 | 94-V0 |
| HY-9300 | Water clear | 1800±800 | / | 1:1 | 1~2 | 12~14 | ≥0.2 | ≥25 | 3.0-3.3 | ≥1.0x10*16 | ≤2.2x10*-4 | 94-V0 |
| HY-9305 | Water clear | 500±100 | 5±3 | 1:1 | 30~60 | 4~5 | ≥0.2 | ≥25 | 3.0-3.3 | ≥1.0x10*16 | ≤2.2x10*-4 | 94-V0 |
| HY-9310 | Water clear | 500±100 | 10±3 | 1:1 | 30~60 | 4~5 | ≥0.2 | ≥25 | 3.0-3.3 | ≥1.0x10*16 | ≤2.2x10*-4 | 94-V0 |
| HY-9320 | Water clear | 1000±100 | 20±3 | 1:1 | 30~60 | 4~5 | ≥0.2 | ≥25 | 3.0-3.3 | ≥1.0x10*16 | ≤2.2x10*-4 | 94-V0 |
| HY-9330 | Water clear | 500±100 | 30±3 | 1:1 | 30~60 | 4~5 | ≥0.2 | ≥25 | 3.0-3.3 | ≥1.0x10*16 | ≤2.2x10*-4 | 94-V0 |
TECHNICAL GUIDELINES
1, Typical Application
It could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
- It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc. Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Mixing Ratio: part A: part B = 1:1
3, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
4, Pls note that the thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100ºC, the silicone will cure in 15 minutes; while in 25ºC room temperature, the silicone will cure around 8 hours.
PACKAGE:
20Kg/pail as a set (Part A 10Kg + Part B 10Kg)
Advantages of Hong Ye Silicone
- 21 years rtv2 silicone factory
- Exported since 2006
- Exports to 138 countries
- 14 years on alibaba.com, 12 years on made-in-china.com, a trustworthy company
- 12 experts of R&D, QC staffs
- 6000 square meter factory
- Free training of silicone technique
- Free silicone samples
- Return and exchange are accepted while quality problems occurred
Any questions about silicone rubber pls fell free to contact Jelly~
whatsup: 00 86 18938867561